Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery

Product Details
Customization: Available
After-sales Service: Provide Reasonable Solutions Within 12 Hours
Warranty: as Required
Still deciding? Get samples of US$ 20/Piece
Request Sample
Gold Member Since 2019

Suppliers with verified business licenses

Audited Supplier

Audited by an independent third-party inspection agency

High Repeat Buyers Choice
More than 50% of buyers repeatedly choose the supplier
Experienced Team
The supplier has 5 foreign trading staff(s) and 3 staff(s) with over 6 years of overseas trading experience
OEM Services
The supplier provides OEM services for popular brands
R&D Capabilities
The supplier has 1 R&D engineers, you can check the Audit Report for more information
to see all verified strength labels (15)
  • Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
  • Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
  • Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
  • Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
  • Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
  • Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
Find Similar Products

Basic Info.

Model NO.
HART-P-200
Type
Steel Plate
Standard
ASTM
Certification
ISO
Surface Treatment
Coated
Technique
Hot Rolled
Application
Container Plate
Special Use
Wear Resistant Steel
Stock
Stock
Wear Resistance
High Wear Abrasion Resistance
Flatness Tolerance
±3mm/M
Impact Resistance
Medium
Hardfacing Layer
High Chromium High Carbide Overlay
Transport Package
Steel Frame or as Required Package
Specification
Stock Thickness: From 3+3 to 30+30mm
Trademark
HART Industry
Origin
Shandong, China
HS Code
7210500000
Production Capacity
1000 Pieces Per Month

Product Description

Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery

Outstanding impact resistant abrasion alloy wear plate for mining machinery

HART Plate is manufactured by depositing chromium-rich, abrasion-resistant materials on mild steel base plate using a traditional arc welding process. This product is usually referred to as chromium carbide overlay (CCO) plate on the market. The hardfacing overlay is suitable for severe abrasive wear and impact applications. Qingdao HART Industrial Technology Co.,Ltd was established in 2003, it had a long history of providing innovative wear solution and world class wear products.

The ultimate hardfaced product for your application depends on the material--whether rock, sand, gravel or other substance--striking or sliding along the surface of your wear part. It also depends on the angle and speed of impact as well as the operating temperature.
NO PRODUCT ITEM DESCRIPTION APPLICATION
1 HART-P-200 Chromium Carbide Overlay Plate Sliding Wear
2 HART-P-100 Chromium Carbide Overlay Plate Severe Sliding Wear
3 HART-P-80 Complex Carbide Overlay Plate Extreme Sliding Wear

Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
 
[Technical Specification Of HART-P-100 ]

1. Base Material:
ASTM A36(Q235B), ASTM A529A(Q345B) , other weldable steel is optional;
Base thickness: 3 to 30 mm
2. Hardfacing Layer: 
Chromium carbon alloy on Fe basis(austenite)
Bulk hardness : >630HV
Mean hardness : >55HRC    
Layer thickness: 3 to 30 mm
3. Welding Processes:
Advanced open arc welding and submerged arc welding
4. Alloy Description: 
Austenitic chrome carbide iron(Chromium white iron)
5. Carbide Hardness:
>
1500HV
6. Volume Fraction of Carbide: 
>30%
7.
Chemical Composition
Carbon:3-6%
Chromium:18-34%

*Various alloys to be used depend on different operating condition and applications.  
Thick C% Cr% Mn% Si% HRC  
3 on 3 3~4 18~20 0.5~1 0.5~1 56~58  
3 on 4 3~4 18~20 0.5~1 0.5~1 56~58  
3 on 5 3~4 18~22 0.5~1 0.5~1 58~60  
3 on N 3.5~4.5 20~25 0.5~1 0.5~1 58~62 N>5
4 on N 3.5~4.5 20~25 0.5~1 0.5~1 58~62
5 on N 4~6 23~25 0.5~1 0.5~1 58~62
6 on N 4~6 24~28 0.5~1 0.5~1 58~62
7 on N 4.5~6 24~28 0.5~1 0.5~1 58~62
8 on N 4.5~6 24~28 0.5~1.5 0.5~1 58~62
9 on N 5~6 26~30 0.5~1.5 0.5~1 60~64
10 on N 5~6 26~30 0.5~1.5 0.5~1 60~64
11 on N 5~6 26~30 0.5~1.5 0.5~1 60~64
12 on N 5~6 26~34 0.5~1.5 0.5~1 60~64
 N on N 5~6 26~34 0.5~2 0.5~1 60~64 N>12

8. Microstructure: 
Composed of a high proportion of extremely hard primary M7C3 chromium rich carbides dispersed in a ductile eutectic austenite matrix.
Maintains 30% to 50% of primary carbides to provide a good wear resistance and homogenous bonding.
Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery

9. Typical Applications: 

HART-P-100 Plate is widely used in the mining, power generation(Coal), cement, dredging, steel production, waste handling, glass production, and pulp and paper industries. Some specific applications include:
INDUSTRY APPLICATONS
Mining Chutes, hoppers, liners for truck beds, dozer blades, shovel buckets, dragline buckets, excavators
Cement Separator guide vanes, discharge cones for clinker storage bins, chutes for sintering ore conveying, outlet ducts for clinker grinding mills, receiving hoppers
Dredging Dredging pipes and pumps, suction pipelines, pump discharges
Steel Dredging pipes and pumps, suction pipelines, pump discharges
Power Coal handling chutes, coal feeder liners, crusher screen plates, classifier cones, journal liners, silo bunkers

10. Wear properties of HART-P-100 (ASTM G65 and SGS test report)
*ASTM G65 is a standard test measuring sliding abrasion resistance using a dry sand/rubber wheel apparatus.
HARDBANDING ALLOY ASTM G65 -- WEIGHT LOSS HARDNESS (Rc)
10+10-8 0.162 g/6000 revs 64.7
10+10-4 0.183 g/6000 revs 63.7
10+10-2 0.149 g/6000 revs 64.0
Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery


11. Service
SERVICE DESCRIPTION
Cutting

1. Can be cut by plasma, laser, water jet, arc gouge, and abrasive saw cutting;
2. Cannot be cut by oxy-fuel.

Welding
1. Use 480 MPa (70 ksi) or 560 MPa (80 ksi) consumable to join base metal;
2. After welding, joint should be capped by overlay for wear protection.
 
Machining
1. Not machinable by conventional methods;
2. Can be finished by grinding only;
3. Countersunk holes can be precisely produced by EDM (Electrical Discharge Machining).
 
Forming
1. Commonly formed with overlay to the inside;
2. For pipes with diameters smaller than 0.6m (24"), hardfacing pipe recommended instead of pipes fabricated from hardfacing plate.
 
Drilling
1. When drilling, the distance between two holes should be at least 15mm (5/8''); otherwise, the partition may not be strong enough and can crack;
2. The minimum diameter of holes should be equal to the thickness of the plates. For thicker plates with a total thickness over 20mm (3/4''), the minimum diameter should be 1.5 times the thickness of the plate.
 

12. Testing and quality control
We documented how the product properties are tested in order to make sure the overlay plates fulfil the specified product properties. Including documentation on 3d party's quality system if calibration and testing is performed by 3d party.
Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery

13. Packing and loading

Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery
Outstanding Impact Resistant Abrasion Alloy Wear Plate for Mining Machinery

 
 

Send your message to this supplier

*From:
*To:
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now
Contact Supplier